In this study we investigated the natural weathering of a catalyzed blend of poly(ethylene terephthalate)/polycarbonate PET/PC (80/20wt/wt%). The results were compared to the accelerated photoaging tests. The specimens were characterized by wide angle X-ray diffraction (WAXD), optical microscopy (OM), thermogravimetry (TG/DTG), medium infrared spectroscopy (FT-IR) and stress-strain analysis. The OM analysis revealed the coexistence of at least three phases – one rich in PET (matrix), the other rich in PC (dispersed droplet) and an interfacial region between them, made of PET/PC copolymer (compatibilizing agent) produced in situ. The TG/DTG curves showed that UV radiation acted mainly on the PET-rich phase and the PET/PC copolymer. The OM and TG/DTG results indicated that the degradation of the compatibilizing agent has had a critical effect on the mechanical properties. For both types of aging (natural and accelerated), the PET’s carbonyl index decreased with the exposure time. The FT-IR results corroborated what was seen in the OM images, showing that the PET phase acts as a shield against the PC degradation. Under accelerated aging, the mechanical properties decreased abruptly - mainly the stress-strain at yield and break - due to the degradation of the in situ compatibilizing agent.

A systematic study of solid state polymerization (SSP), concerning the melt extruded blend of poly(ethylene terephthalate)/polycarbonate (catalyzed PET/PC, 80/20 wt %), as a function of temperature range (180-190°C) for a fixed time (6 h) is presented. The materials obtained were evaluated by differential scanning calorimetry (DSC), thermogravimetry/derivative thermogravimetry (TG/DTG), optical microscopy (OM) and intrinsic viscosity (IV) analysis. After SSP, at all reaction temperatures, PET glass transition and heating crystallization temperatures slightly decreased, melting temperature slightly increased, while degree of crystallinity was practically invariable. The DTG curves indicated that, at least, three phases remained. The OM images revealed that the morphology is constituted of a PET matrix and a PC dispersed phase. In the interfacial region we noticed the appearance of structures like bridges linking the matrix and the dispersed domains. These bridges were correlated to the PET/PC block copolymer obtained during blending in the molten state. IV increased for all polymerization temperatures, due to the occurrence of PET chain extension reactions - esterification and transesterification. The IV range for bottle grade PET was achieved.

Composites of recycled high density polyethylene (HDPE-R) and coffee dregs (COFD) were elaborated. The blends were made at the proportions of 100-0, 90-10, 80-20, 70-30, 60-40, 50-50 and 40-60% polymer-filler ratio. The materials were evaluated through scanning electron microscopy (SEM), differential scanning calorimetry (DSC), thermogravimetry/derivative thermogravimetry (TGA), and compressive resistance test. The compounding was done using a two-stage co-kneader system extruder, and then cylindrical specimens were injection molded. All composites had a fine dispersion of the COFD into the polymeric matrix. The composites degraded in two steps. The first one was in a temperature lower than the neat HDPE, but higher than the average processing temperature of the polymer. The melting temperature and the degree of crystallinity of the composites resulted similar to the neat HDPE ones. The compressive moduli of the composites resulted similar to the neat polymer one. The results show that these composites have interesting properties as a building material.